cutback bitumen MC-30

Cutback bitumen MC-30

 

 

 

General information of cutback bitumen MC-30

In many places, cutback asphalt use is restricted to patching materials for use in cold weather cutback MC-30 is medium curing (MC) cut-back asphalt consisting of penetration grade asphalt cement and diluent or cutter of medium volatility. The diluent temporarily reduces the viscosity of the asphalt cement for ease of handling and application. Cutback MC-30 use in the road maintenance industry where it is used as a prime coat of the base course prior to placing of the bituminous surface course. Its purpose is to bind the granular material of the base course to the asphalt layer. Usual application is by spray using a distributor.

Cutback bitumen MC-30 is dissolved of bitumen in solvents of kerosene. In many countries, kerosene and other volatile petroleum-derived products are added as a cutter or cutback agent to bitumen to reduce (or cutback) the viscosity of the bitumen. The mixture obtained may be called cutback bitumen.

Our MC-30 Cutback Bitumen complies with cutback petroleum asphalts of the Medium-Curing type for use in the construction and treatment of pavements as per ASTM D2028-97 reapproved in 2004. Cutback Grade Bitumen is normally used in spraying and in some mixing applications. Cutback Bitumen is penetration grade bitumen blended with a solvent such as kerosene, white spirit, gasoline, and naphtha, controlling the curing time. Cut back petroleum asphalts of the rapid curing type supplied by BITUMENSHOP Co are petroleum grade bitumen manufactured from the fractional / vacuum distillation of crude oil blended with a solvent. Bitumen supplied by BITUMENSHOP Co is produced from the vacuum residue (short residue) feedstock. Penetration Grade bitumens are specified by the penetration and softening point test. Designation is by penetration range only. The penetration grade bitumens have a thermoplastic property which causes the material to soften at high temperatures and to harden at lower temperatures. This unique temperature/ viscosity relationship is important when determining the performance parameters such as the adhesion, rheology, durability, and application temperatures of bitumen. The cutback bitumen (Asphalts) supplied by BITUMENSHOP are blended from petroleum grade bitumen as stated herein

Uses of cutback bitumen MC-30

Cutback agents are used to lower the viscosity of bitumen when it is applied as a primer to the surface of a road pavement aggregate base course or substrate. Kerosene is used as a bitumen cutback agent at different concentrations according to local conditions and requirements.

The cutback bitumen is ideal for prime coat and cold applied because of easy uses and no need to thinning and heating.

Cutback bitumen MC-30 consist of initial incorporation of asphalt into the surface of non-asphalt based course preparatory to any superimposed treatment of construction.

The cutback asphalt MC-30 applying to waterproofing of surfaces, plug capillary voids, coat and bond loose mineral particles.

Current common uses are in penetrating prime coats and in producing patching or stockpile mixtures. Cutback asphalt used in mixing with aggregate will usually contain an adhesion agent to assist in the coating of the aggregate surface.

Packing of cutback bitumen MC-30

This cutback bitumen bulk in the tanker and also in new steel and thick drum on the pallet to prevent all leak inside of the container.

Safety of cutback bitumen MC-30

Refer to Safety Data sheets before use.
Transport, use and store at the lowest temperature possible.
Eliminate all potential ignition sources during application.
Avoid breathing vapors. Avoid contact with skin.
Always wear appropriate PPE including heat protection when used hot.
DO NOT allow product or washings to enter stormwater or sewer systems.

Specification of cutback bitumen MC-30

BITUMENSHOP  Co. guarantees that the Medium Curing Cutback Grade MC-30 it supplies under its offers is produced in compliance to and is in conformity to ASTM D-2028-97 Rev 2004 and is compliant to the following specification requirements.

property

specification limit

 Test method

Min

Max

Kinematic viscosity at 60°c ,cST

30

60

ASTM D2170

Flash point(tag open cup), °C

38

— 

ASTM D3143

Distillation test
Distillate, volume percent of total Distillate to
680°F (360°C)

to 437°F (225°C)
To
500°F (260°C)
to
600°F (316°C)
Residue from distillation to
680°F(360°C), percent volume by difference

— 

25

 

ASTM D402

 

30

75

75

95

50

— 

Test on Residue from distillation test

Viscosity at 140°F (60°C)

30

120

ASTM D2170

Penetration 77°F (25°C) 100g,5s mm

120

300

ASTM D5

Ductility 77°F (25°C) 5cm/min cm

100

— 

ASTM D113

Solubility in trichloroethylene %

99

— 

ASTM D2042

Water, percent volume

— 

0.2

ASTM D95

 

 